Room temperature thermally evaporated thin Au film on Si suitable for application of thiol self-assembled monolayers in MEMS/NEMS sensors

Mahmoodi, Nasim; Rushdi, Abduljabbar I.; Bowen, James; Sabour, Aydin; Anthony, Carl; Mendes, Paula M. and Preece, Jon A. (2017). Room temperature thermally evaporated thin Au film on Si suitable for application of thiol self-assembled monolayers in MEMS/NEMS sensors. Journal of Vacuum Science and Technology A, 35(4), article no. 041514.

Full text available as:
[img]
Preview
PDF (Accepted Manuscript) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
Download (845kB) | Preview
DOI (Digital Object Identifier) Link: https://doi.org/10.1116/1.4990026
Google Scholar: Look up in Google Scholar

Abstract

Gold is a standard surface for attachment of thiol-based self-assembled monolayers (SAMs). To achieve uniform defect free SAM coatings, which are essential for bio/chemical sensing applications, the gold surface must have low roughness, and be highly orientated. These requirements are normally achieved by either heating during Au deposition or post deposition Au surface annealing. This paper shows that room temperature deposited gold, can afford equivalent gold surfaces, if the gold deposition parameters are carefully controlled. This observation is an important result as heating (or annealing) of the deposited gold can have a detrimental effect on the mechanical properties of the silicon on which the gold is deposited used in microsensors. The paper presents the investigation of the morphology and crystalline structure of Au film prepared by thermal evaporation at room temperature on silicon. The effect of gold deposition rate is studied, and it is shown that by increasing the deposition rate from 0.02 nm s-1 to 0.14 nm s-1 the gold surface RMS roughness decreases, whereas the grain size of the deposited gold is seen to follow a step function decreasing suddenly between 0.06 and 0.10 nm s-1. The XRD intensity of the preferentially [111] orientated gold crystallites is also seen to increase as the deposition rate increases up to a deposition rate of 0.14 nm s-1. Formation and characterization of 1-dodecanethiol on these Au coated samples is also studied using contact angle. It is shown that by increasing the Au deposition rate the contact angle hysteresis (CAH) decreases until it plateaus, for a deposition rate greater than 0.14 nm s-1, where the CAH is smaller than 9 degrees which is an indication of homogeneous SAM formation, on a smooth surface.

Item Type: Journal Item
Copyright Holders: 2017 American Vacuum Society
ISSN: 0734-2101
Extra Information: 12 pp.
Keywords: gold; metallic thin films; self assembly; X-ray diffraction; topography
Academic Unit/School: Faculty of Science, Technology, Engineering and Mathematics (STEM) > Engineering and Innovation
Faculty of Science, Technology, Engineering and Mathematics (STEM)
Item ID: 49643
Depositing User: James Bowen
Date Deposited: 04 Jul 2017 10:40
Last Modified: 04 Jul 2017 10:40
URI: http://oro.open.ac.uk/id/eprint/49643
Share this page:

Altmetrics

Download history for this item

These details should be considered as only a guide to the number of downloads performed manually. Algorithmic methods have been applied in an attempt to remove automated downloads from the displayed statistics but no guarantee can be made as to the accuracy of the figures.

Actions (login may be required)

Policies | Disclaimer

© The Open University   contact the OU