Neutron diffraction measurements of residual stress in a powder metallurgy component

Schneider, L.C.R.; Hainsworth, S.V.; Cocks, A.C.F. and Fitzpatrick, M.E. (2005). Neutron diffraction measurements of residual stress in a powder metallurgy component. Scripta Materialia, 52(9) pp. 917–921.

DOI (Digital Object Identifier) Link: https://doi.org/10.1016/j.scriptamat.2004.12.030
Google Scholar: Look up in Google Scholar

Abstract

Residual stresses in a typical industrial green component were determined using neutron diffraction. The measured residual stresses were found to correlate with cross-sectional variations. Residual stress at the edge of the compact in contact with the die wall during compaction reached up to +80 MPa (tension) and −100 MPa (compression).

Item Type: Journal Item
ISSN: 1359-6462
Academic Unit/School: Faculty of Science, Technology, Engineering and Mathematics (STEM) > Engineering and Innovation
Faculty of Science, Technology, Engineering and Mathematics (STEM)
Item ID: 4735
Depositing User: Michael E. Fitzpatrick
Date Deposited: 11 Jul 2006
Last Modified: 02 Nov 2017 15:05
URI: http://oro.open.ac.uk/id/eprint/4735
Share this page:

Altmetrics

Actions (login may be required)

Policies | Disclaimer

© The Open University   contact the OU