In situ neutron diffraction study of texture evolution and variant selection during the α→β→α phase transformation in Ti–6Al–4V

Obasi, G.C.; Moat, R.J.; Leo Prakash, D.G.; Kockelmann, W.; Quinta da Fonseca, J. and Preuss, M. (2012). In situ neutron diffraction study of texture evolution and variant selection during the α→β→α phase transformation in Ti–6Al–4V. Acta Materialia, 60(20) pp. 7169–7182.

DOI (Digital Object Identifier) Link: http://dx.doi.org/10.1016/j.actamat.2012.09.026
Google Scholar: Look up in Google Scholar

Abstract

In the present study, in situ phase transformation experiments have been carried out using neutron diffraction to monitor the texture evolution during the α → β → α phase transformation in Ti–6Al–4V with and without 0.4% yttrium additions. The aim of adding yttrium was to control β grain growth above the β transus by Zener pinning. First, both alloys were thermomechanically processed to generate a similar starting α texture and grain morphology. Subsequently, both materials were heat treated above the β transus up to 1250 °C followed by furnace cooling to 210 °C to promote diffusional phase transformation starting from β grain boundaries. In situ texture measurements were taken during α → β → α phase transformation starting at room temperature, 800 °C, 950 °C, above β transus (1050 and 1250 °C), and back to near room temperature. The degree of variant selection was determined by comparing the predicted transformation texture during heating and cooling based on the Burgers relationship and the assumption of no variant selection with the measured textures. It was found that during heating β grows from the pre-existing β and that the β texture evolved even before the β transus was exceeded. The β texture strengthened noticeably above the β transus in the case of conventional Ti–6Al–4V but not Ti–6Al–4V–0.4Y, which was related to β grain coarsening. The level of variant selection was clearly affected by grain coarsening and the formation of β texture components that contribute to the 〈1 1 1〉//normal direction (ND) γ fibre texture rotated about 10° away from ND.

Item Type: Journal Article
Copyright Holders: 2012 Acta Materialia Inc.
ISSN: 1359-6454
Keywords: titanium alloys; texture evolution; neutron diffraction; variant selection
Academic Unit/Department: Mathematics, Computing and Technology > Engineering & Innovation
Item ID: 34805
Depositing User: Richard Moat
Date Deposited: 29 Oct 2012 16:31
Last Modified: 13 Mar 2013 14:19
URI: http://oro.open.ac.uk/id/eprint/34805
Share this page:

Actions (login may be required)

View Item
Report issue / request change

Policies | Disclaimer

© The Open University   + 44 (0)870 333 4340   general-enquiries@open.ac.uk